Fluorine Doped Tin Oxide Coated Glass (FTO)
Surface resistance < 10 Ohm/sq
Size: 100 mm x 100 mm
Thickness: 2.2 mm Optical
Transmittance > 83%
Temperature ~600 Degree °C
Haze: 3-5%
FTO Coating Thickness ~450 nm
Fluorine Doped Tin Oxide Coated Glass (FTO)
Surface resistance < 10 Ohm/sq
Size: 20 mm x 20 mm Thickness: 2.2 mm
Optical Transmittance > 83%
Temperature ~600 Degree °C
Haze: 3-5%
FTO Coating Thickness ~450 nm
Fluorine Doped Tin Oxide Coated Glass (FTO)
Surface resistance < 10 Ohm/sq
Size: 25 mm x 25 mm
Thickness: 2.2 mm
Optical Transmittance > 83%
Temperature ~600 Degree °C
Haze: 3-5%
FTO Coating Thickness ~450 nm
Fluorine Doped Tin Oxide Coated Glass (FTO)
Surface resistance < 10 Ohm/sq
Size: 50 mm x 50 m
Thickness: 2.2 mm
Optical Transmittance > 83%
Temperature ~600 Degree °C
Haze: 3-5%
FTO Coating Thickness ~450 nm
IDE Interdigitated (ITO) electrode on Glass
Sheet Resistance: < 10 Ohm/sq
Optical Transmittance: > 84%
Substrate: Soda Calcium Glass
Size: 20 mm x 15 mm
Thickness: 1.1 mm
Coating Process: Magnetron Sputtering
ITO Coating Thickness: ~185 nm
Electrode Line Width: 80 µm
Line Spacing: 80 µm
Finger Length: 8.5 mm
Indium Tin Oxide Coated Glass (ITO)
Sheet Resistance < 10 Ohm/sq
Size: 100mm x 100mm
Thickness: 1.1 mm
Optical Transmittance > 84%
Working Temperature 300 °C
ITO Coating Thickness ~185 nm
Indium Tin Oxide Coated Glass (ITO)
Sheet Resistance < 6 Ohm/sq
Size: 100mm x 100mm
Thickness: 1.1 mm
Optical Transmittance > 83%
Working Temperature 300 °C
ITO Coating Thickness ~260 nm
Indium Tin Oxide Coated Glass (ITO)
Sheet Resistance < 10 Ohm/sq
Size: 20mm x 20mm
Thickness: 1.1 mm
Optical Transmittance > 84%
Working Temperature 300 °C
ITO Coating Thickness ~185 nm
Indium Tin Oxide Coated Glass (ITO)
Sheet Resistance < 10 Ohm/sq
Size: 50mm x 50mm
Thickness: 1.1 mm
Optical Transmittance > 84%
Working Temperature 300 °C
ITO Coating Thickness ~185 nm
Indium Tin Oxide Coated Glass (ITO)
Sheet Resistance < 6 Ohm/sq
Size: 50mm x 50mm
Thickness: 1.1 mm
Optical Transmittance > 83%
Working Temperature 300 °C
ITO Coating Thickness ~260 nm
Indium Tin Oxide Coated Glass (ITO)
Sheet Resistance ~ 9-11 Ohm/sq
Size: 200 mm x 300 mm
Thickness: 125 micron
Optical Transmittance ~ 86%
ITO coating thickness: 20 – 40 nm*
Quartz Glass Substrate
Size: 100mm x 100mm
Thickness: 1mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃
Quartz Glass Substrate
Size: 100mm x 100mm
Thickness: 2mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃
Quartz Glass Substrate
Size: 20mm x 20mm
Thickness: 1mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃
Quartz Glass Substrate
Size: 20mm x 20mm
Thickness: 2mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃
Quartz Glass Substrate
Size: 25mm x 25mm
Thickness: 1mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃
Quartz Glass Substrate
Size: 25mm x 25mm
Thickness: 2mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃
Quartz Glass Substrate
Size: 50mm x 50mm
Thickness: 1mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃
Quartz Glass Substrate
Size: 50mm x 50mm
Thickness: 2mm
Optical Transmittance range (JGS2): 200-2500nm
Short time working temperature: 1250℃
Long time working temperature: 1050℃