Aluminium (Al) Sputtering Target

Diameter: 2 Inch ± 0.02 Inch
Thickness: 3 mm ± 0.1 mm
Purity: 99.99%
Melting Point (°C): 660
Theoretical Density (g/cc): 2.7
Sputtering: DC

Gold (Au) Sputtering Target

Diameter: 2 Inch / 3 Inch / as required
Thickness 1 mm / 2 mm / as required
Purity 99.99%
Melting Point (°C): 1064
Theoretical Density (g/cc): 19.32
Sputtering: DC

Aluminum Oxide (Al2O3) Sputtering Target

Diameter: 2 Inch / 3 Inch / as required
Thickness 2 mm / 3 mm / as required
Purity 99.99% / as required
Melting Point (°C): 2072
Theoretical Density (g/cc): 3.97
Sputtering: RF
with or without Copper backing plate

Platinum (Pt) Sputtering Target

Diameter: 2 Inch / 3 Inch / as required
Thickness 1 mm / 2 mm / as required
Purity 99.95%
Melting Point (°C): 1772
Theoretical Density (g/cc): 21.45
Sputtering: DC

Titanium (Ti) Sputtering Target

Diameter: 2 Inch / 3 Inch / as required
Thickness 2 mm / 3 mm / as required
Purity 99.99% / as required
Melting Point (°C): 1660
Theoretical Density (g/cc): 4.5
Sputtering: DC

Titanium Dioxide (TiO2) Sputtering Target

Diameter: 2 Inch / 3 Inch / as required
Thickness 2 mm / 3 mm / as required
Purity 99.99% / as required
Melting Point (°C): 1830
Theoretical Density (g/cc): 4.23
Sputtering: RF
with or without Copper backing plate

Tungsten Oxide (WO3) Sputtering Targets

Diameter: 2 Inch / 3 Inch / as required
Thickness 2 mm / 3 mm / as required
Purity 99.99% / as required
Melting Point (°C): 1473
Theoretical Density (g/cc): 7.16
Sputtering: RF
with or without Copper backing plate

Zinc (Zn) Sputtering Target

Diameter: 2 Inch ± 0.02 Inch
Thickness: 2 mm ± 0.1 mm
Purity: 99.99%
Melting Point (°C): 419.5
Theoretical Density (g/cc): 7.14
Sputtering: DC

Zinc Oxide (ZnO) Sputtering Target

Diameter: 2 Inch / 3 Inch / as required
Thickness 2 mm / 3 mm / as required
Purity 99.99% / as required
Melting Point (°C): 1975
Theoretical Density (g/cc): 5.61
Sputtering: RF
with or without Copper backing plate

Tin (Sn) Sputtering Target

Diameter: 2 Inch ± 0.02 Inch
Thickness: 3 mm ± 0.1 mm
Purity: 99.99%
Melting Point (°C): 232
Theoretical Density (g/cc): 7.28
Sputtering: DC