Copper Foam

Dimension 200 x 300 mm
Specification 110 ppi
Porosity 95%

Nickel Foam

Dimension 200 x 300 cm

Porosity 95%-98%
Open Cell Rate ≥98 %
Volume Density >0.1g/cm3, as per request
Surface Density 200-3500 g/m 2, as per request

Standard: 320±20g/m2
Thermal Conductivity (Theoretical) >3W/M.K
Mechanical Strength (Theoretical) ≥2~7MPa

Nickel Foam

Dimension cutomisable

Type Open cell
Purity > 99.99%
Form Sheet or Roll, depending on size & thickness
Cell Size (PPI) 5-1300PPI, as per request
Thickness Standard: 0.08-30mm
Size & Shape POR
Porosity 95%-98%
Open Cell Rate ≥98 %
Volume Density >0.1g/cm3, as per request
Surface Density 200-3500 g/m 2, as per request

Standard: 320±20g/m2
Thermal Conductivity (Theoretical) >3W/M.K
Mechanical Strength (Theoretical) ≥2~7MPa
Average Tensile Strength (N/20mm) Vertical ≥ 30, horizontal ≥ 25
Temperature Resistance (Theoretical) ≥500℃,as per request
Appearance Silver gray, without defects such as black spots, blind holes, through holes, cracks, etc
Chemical Composition Ni: ≥99.5% Fe≤0.020% C≤0.030% P≤0.010%  S≤0.008%  Si≤0.005% Cu≤0.010%
Shielding Effectiveness 200KHz
40dB~50dB
Flexibility Vertical ≥ 5, horizontal ≥ 15
Elongation rate (%) Vertical ≥ 5, horizontal ≥ 10
Electrical resistivity (m Ω/100 * 10m2) Vertical ≤ 65, horizontal ≤85

Aluminium Foam

Laboratory Titanium Foam Ti Metal Foam For Electrode Sheet

Filtration accuracy 0.45um-100um
Porosity 28-50%
Transmittance rate 0.02-20M3cm/m2h.mmH2O
Compressive strength 0.5-1.5Mpa
Temperature resistance 280 ° C (wet state)
Maximum working pressure range 0.6Mpa
Precision 0.22 µm 0.45 µm 1 µm 3 µm 5 µm 10 µm 20 µm 30µm  50 µm 80 µm 100 µm

Nickel-Silver Alloy Foam Can Customizable Large Pore Size

Thickness 0.1mm to 10mm，customizable
Porosity ≥95%
Length 100mm，customizable
Width 100mm，customizable
Net Weight 21g
Specific Surface area ≥10 square / g
Tensile Strength Lengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2

Ag-Ni Alloy Foam Silver Metal Foam Have Big Pore size

Times 0.1mm to 10mm，customizable
Porosity ≥95%
Length 100mm，customizable
Width 100mm，customizable
Net Weight 21g
Specific Surface area ≥10 square / g
Tensile Strength Lengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2

Customizable Size Silver Foam on Nickel Base 15%Ni and 85%Ag

Thickness 0.1mm to 10mm，customizable
Porosity ≥95%
Length 100mm，customizable
Width 100mm，customizable
Net Weight 21g
Specific Surface area ≥10 square / g
Tensile Strength Lengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2

High Purity Silver Metal Foam

Thickness 0.1mm to 10mm，customizable
Porosity ≥95%
Length 100mm，customizable
Width 100mm，customizable
Net Weight 21g
Specific Surface area ≥10 square / g
Tensile Strength Lengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2

99.9%_ Purity Sintered SS Foam Stainless Steel Metal Foam

Diameter Ф5-Ф300 (mm)
Thickness 0.5-10mm
Filtration accuracy 0.5un-70um
Material 302 304 304L 321 316 316L 310S
Porosity 20-50％
Permeability 3-1300m3/m3hkPa
Compressive strength 3Mpa
Temperature resistance 500℃
Maximum working pressure 0.6Mpa
Shape Rectangle, Circular, Tube, Cylinder

(SS) Stainless Steel Metal Foam Material

Diameter Ф5-Ф300 (mm)
Thickness 0.5-10mm
Filtration accuracy 0.5un-70um
Material 302 304 304L 321 316 316L 310S
Porosity 20-50％
Permeability 3-1300m3/m3hkPa
Compressive strength 3Mpa
Temperature resistance 500℃
Maximum working pressure 0.6Mpa
Shape Rectangle, Circular, Tube, Cylinder

0.7 to 3mm Thickness Sintered SS Stainless Steel Foam Sheet

Diameter Ф5-Ф300 (mm)
Thickness 0.5-10mm
Filtration accuracy 0.5un-70um
Material 302 304 304L 321 316 316L 310S
Porosity 20-50％
Permeability 3-1300m3/m3hkPa
Compressive strength 3Mpa
Temperature resistance 500℃
Maximum working pressure 0.6Mpa
Shape Rectangle, Circular, Tube, Cylinder

1.2MM~1.6MM Thickness 3D Graphene Foam

Sample size 100*100mm
Thickness 1.2 mm-1.6mm
Density 4 mg/cm3
Pore Size 580 microns
Packing  in sealed membrane box
Surface density 0.5-0.9 mg/cm2.
Size of branches 50-200 microns
Characteristic of  large aperture 200-500 microns.
Thermal conductivity ＞6w/(m2k)
Standard PPI value 110

High Purity Large Aperture 3D Graphene Foam

Sample size 100*100mm
Thickness 1.2 mm-1.6mm
Density 4 mg/cm3
Pore Size 580 microns
Packing  in sealed membrane box
Surface density 0.5-0.9 mg/cm2.
Size of branches 50-200 microns
Characteristic of  large aperture 200-500 microns.
Thermal conductivity ＞6w/(m2k)
Standard PPI value 110

Size Customizable 3D Graphene Foam Sheet

Sample size 100*100mm  （can be customized）
Thickness 1.2 mm-1.6mm
Density 4 mg/cm3
Pore Size 580 microns
Packing  in sealed membrane box
Surface density 0.5-0.9 mg/cm2.
Size of branches 50-200 microns
Characteristic of  large aperture 200-500 microns.
Thermal conductivity ＞6w/(m2k)
Standard PPI value 110

99.5% Purity Graphene Metal Foam C(n) Metal Foam

Sample size 100*100mm  （can be customized）
Thickness 1.2 mm-1.6mm
Density 4 mg/cm3
Pore Size 580 microns
Packing  in sealed membrane box
Surface density 0.5-0.9 mg/cm2.
Size of branches 50-200 microns
Characteristic of  large aperture 200-500 microns.
Thermal conductivity ＞6w/(m2k)
Standard PPI value 110

Customizable Profiled Carbon Fiber Foam

Thickness 0.1-25mm
Pore Size(PPI) 15/20/30/50/90/100
Purity(%) 99.99
Porosity(%) 50-98
Surface desity(g/m2) 280-3000
Size(mm) 10×10, 50×50,100×100, 200×200,

Can be customized
Density(g/cm3) 0.2~1.0
Compressive strength(Mpa) 8~12
Tensile modulus(Mpa) 300~500
Thermal expansion coefficient (ppm/℃) 5.0
Thermal conductivity(W/m.k) 25~80
Resistivity(Ω·m) 1.0×10﹣2~10﹣5
Maximum operating temperature 600 ℃ (in air)

3000 ℃ (in inert gas)

0.01~6mm Aperture Reticulated Carbon Foam

Thickness 0.1-25mm
Pore Size(PPI) 15/20/30/50/90/100
Purity(%) 99.99
Porosity(%) 50-98
Surface desity(g/m2) 280-3000
Size(mm) 10×10, 50×50,100×100, 200×200,

Can be customized
Density(g/cm3) 0.2~1.0
Compressive strength(Mpa) 8~12
Tensile modulus(Mpa) 300~500
Thermal expansion coefficient (ppm/℃) 5.0
Thermal conductivity(W/m.k) 25~80
Resistivity(Ω·m) 1.0×10﹣2~10﹣5
Maximum operating temperature 600 ℃ (in air)

3000 ℃ (in inert gas)

Size Customizable Carbon Metal Foam Electrode

Thickness 0.1-25mm
Pore Size(PPI) 15/20/30/50/90/100
Purity(%) 99.99
Porosity(%) 50-98
Surface desity(g/m2) 280-3000
Size(mm) 10×10, 50×50,100×100, 200×200,

Can be customized
Density(g/cm3) 0.2~1.0
Compressive strength(Mpa) 8~12
Tensile modulus(Mpa) 300~500
Thermal expansion coefficient (ppm/℃) 5.0
Thermal conductivity(W/m.k) 25~80
Resistivity(Ω·m) 1.0×10﹣2~10﹣5
Maximum operating temperature 600 ℃ (in air)

3000 ℃ (in inert gas)

High Temperature and Corrosion Resistant Carbon Metal Foam

Thickness 0.1-25mm
Pore Size(PPI) 15/20/30/50/90/100
Purity(%) 99.99
Porosity(%) 50-98
Surface desity(g/m2) 280-3000
Size(mm) 10×10, 50×50,100×100, 200×200,

Can be customized
Density(g/cm3) 0.2~1.0
Compressive strength(Mpa) 8~12
Tensile modulus(Mpa) 300~500
Thermal expansion coefficient (ppm/℃) 5.0
Thermal conductivity(W/m.k) 25~80
Resistivity(Ω·m) 1.0×10﹣2~10﹣5
Maximum operating temperature 600 ℃ (in air)

3000 ℃ (in inert gas)

High Purity Porous Iron Foam Iron Metal Foam

Item Producible specifications Reference specifications
PPI 8-110(±2/5/10） 110±10 13±2
Surface density (g/m2) 250-5000(±5%） 380±25 2000±100
size（mm) 20-1000(±0.5/1.0/2.0） 500±0.5 500±2
Appearance Silver gray, without black spot, blind spot, through hole and crack
Chemical Composition           Pure Iron (Fe):≤99.9%
(C):≤0.030% (S):≤0.008%
(Si):0.005% (Cu):≤0.005%

0.5mm-25mm Thickness Porous Iron Foam Fe Metal Foam For Lab Research

Item Producible specifications Reference specifications
PPI 8-110(±2/5/10） 110±10 13±2
Surface density (g/m2) 250-5000(±5%） 380±25 2000±100
size（mm) 20-1000(±0.5/1.0/2.0） 500±0.5 500±2
Appearance Silver gray, without black spot, blind spot, through hole and crack
Chemical Composition           Pure Iron (Fe):≤99.9%
(C):≤0.030% (S):≤0.008%
(Si):0.005% (Cu):≤0.005%

High Purity Cobalt Metal Foam

Thickness range 0.8-2mm
PPI range 110ppi
Porosity 95-98%
Through hole ratio ≥ 98%
Aperture 0.23mm
Area density 100-2000 g / m2
Bulk density 0.1-2.0g/cm3